Technical data:
Skin-forming time at 23 °C / 50% r.h. - 15 min
Density at 23 °C - 1,01 g/cm3 (ISO 1183, methode A)
Extrusion rate at 23°C - 450 ml/min
Tensile strength - 0,5 N/mm2 (ISO 8339)
Elongation at break - 250 % (ISO 8339)
Modulus at 100% elongation - 0,34 N/mm2 (ISO 8339)
********Hardness, Shore A******** - 18 (ISO 868)
Tear strength - 4,0 N/mm (ISO 34, method C)
Movement capability - 25 % (ISO 11 600)
Skin-forming time at 23 °C / 50% r.h. - 15 min
Density at 23 °C - 1,01 g/cm3 (ISO 1183, methode A)
Extrusion rate at 23°C - 450 ml/min
Tensile strength - 0,5 N/mm2 (ISO 8339)
Elongation at break - 250 % (ISO 8339)
Modulus at 100% elongation - 0,34 N/mm2 (ISO 8339)
********Hardness, Shore A******** - 18 (ISO 868)
Tear strength - 4,0 N/mm (ISO 34, method C)
Movement capability - 25 % (ISO 11 600)
Proposed translations
(Latvian)
5 +1 | cietība, pēc Šora (A) | Janis Veveris (Mr.) |
Proposed translations
+1
52 mins
Selected
cietība, pēc Šora (A)
4 KudoZ points awarded for this answer.
Comment: "Paldies!"
Something went wrong...